主要以生物基戊二胺和石油基己二酸聚合而成，生物基含量高达47%-100%以上。 其中，PA510是通过将来自蓖麻油植物的癸二酸（生物基癸二酸）和来自玉米的五亚甲基二胺（生物基1,5-戊二胺）进行聚合得到，生物基含量高达100%。
It is mainly polymerized from biobased glutaric amine and petroleum-based adipic acid, with a biobased content of up to 47%-100%. PA510 is produced through the polymerization of sebacic acid (biobased sebacic acid) derived from castor oil plants and pentamethylene diamine (biobased 1,5-pentanediamine) from corn, ，with a biobased content reaching 100%
Green Password
Natural performance, green technology, carbon reduction, and environmental protection
Green substrate
Using biological substrates as raw materials, environmentally friendly and renewable
Biological Fermentation
Advanced genetic modification technology, efficient and high-purity strain transformation
Purification
Advanced purification technology for better product extraction efficiency and higher purity
Polymerization
Create a complete set of automatic biological matrix aggregation devices
Fibre
Green bio based products can process various types of civil silk, industrial silk, BCF carpet silk, short fibers, etc
Fnish Product
Natural material, comfortable and soft, low-temperature dyeing, energy-saving and environmentally friendly
Product Performance
99.99% Bio -based
Made from sebacic acid in castor oil plants and pentamethylenediamine in corn
Low Moisture Absorption
PA510 has a moisture regain rate of 2.5%,
PA6 has a moisture regain rate of 3.5-4.0%,
PA66 has a moisture regain rate of 4.0-4.5%
High color fastness and not easy to fade
PA510, PA6, and PA66 have less color fastness to soap washing compared to PA6/PA66
High strength and wear resistance
Strength comparable to nylon 66 and excellent wear resistance
Stable size
The shrinkage rate of boiling water is around 3%, The moisture regain of PA510 is 2.5% lower than that of conventional nylon materials, PA6 regain rate 3.5-4.0%, PA66 regain rate 4.0-4.5%